The PVC Coating on these particular sheets can be done on single side as well as both sides. The carefully controlled multistage pretreatment process ensures a high receptive surface to which the PVC furniture film (fire retardant) adheres strongly. The bonding is then reinforced with the use of specially develpoed and tested resin.
Optimum conditions of manufacturing and meticulous quality control assure a superior sheet. The PVC coated Aluminium and GP sheet can effectively withstand the rigorous of host of industrial applications.
Salient Features of Our Products :
Our PVC coated sheets can be subjected to any steel-forming process like
Bending
Drilling
Shearing
Punching
Crimping
without effecting its colourful patterns.
Our PVC coated sheets are
Fire retardant
Scratch resistant
Aberration resistant
Rust Free
Washable.
and having long life which contributes to cost reduction and saving in labur with additional advantage of high productivity and eliminating cost of refurninshing & repainting
Product Specifications
Base Metal :
Type of steel Sheet Thickness (mm)
Aluminium 0.4 mm to 1.2 mm
GP 0.4 mm to 0.9 mm
MDF/Plywood/Foam 3 mm to 6 mm
Coating Material :
Type of steel Sheet Thickness (mm)
PVC Film 0.17mm to 0.25mm
PET Film 0.13mm to 0.20mm
Size:
Configuration Width (mm) Length (mm)
Normal Tolerance Normal Tolerance
Cut Sheet 765-1250 ±1.0 1500-3040 ±1.0
Standard Size Availabilities 765 / 914 / 1220
Technical Testing Data for PVC/PET Coated sheet
TEST RESULT & OBSERVATION.
Abrasion Resistance (cc) Tested after 7000 cycle Withstands protection to base substrate
Scratch resistance Withstands 5Kg 1mm Ball indenting.
Flexibility at Low temperature Shall not break / crack or show any other sign of failure
Heat cycle durability Neither delamination nor colour change is observed.
Colour Fastness to day light No colour fading, Suitable for interior applications.
Stain Resistance Product are normally resistant to sprit. tea, coffee, thinner, wine. ketchup, vinegar, Soya sauce
Chemical resistance No effect of Ethyl alcohol, 10% HCL, 10% NaOH, Ammonia Water, Alkali Aqueous solutions.
Flammability Burning rate is not more than 100 mm/minute.
Peel Strength >1.25 N/MM